Introduction to fused zirconium corundum brick(AZS Bricks):
Electric fused zirconium corundum bricks, also called Fused AZS bricks, are arranged according to the three chemical components in the phase diagram of Al2O3-ZrO2-SiO2. Among them, 33, 36 and 41 are named according to the content of Al2O3. For example, AZS33 refers to the fused zirconium corundum brick with an alumina content of 33%.
Parameters of Kerui Fused AZS Bricks
| ltem | AZS-33 | AZS-33 | AZS-36 | AZS-36 | AZS-41 | AZS-41 |
| – | Y | H | Y | H | Y | H |
| Al2O3, ≥ | 50 | 50.5 | 48 | 49 | 45 | 45.5 |
| ZrO2, ≥ | 32.0 | 32.0 | 35.0 | 35.0 | 40.0 | 40.0 |
| SiO2, ≤ | 15.0 | 16.0 | 13.5 | 13.5 | 13.0 | 12.0 |
| Na2O, ≤ | 1.5 | 1.5 | 1.4 | 1.4 | 1.3 | 1.3 |
| BD, PT.QX, ≥ | 3.40 | 3.30 | 3.45 | 3.40 | 3.55 | 3.50 |
| BD, MS, ≤ | 3.50 | 3.45 | 3.60 | 3.55 | 3.70 | 3.65 |
| BD, WS, ≤ | 3.60 | 3.55 | 3.70 | 3.65 | 3.80 | 3.75 |
AZS-33 Bricks
AZS-33 bricks has good corrosion resistance to liquid glass, is not easy to produce stones or other defects, and has low possibility of producing small bubbles. Therefore, AZS-33 bricks are widely used in glass kilns, mainly applicable to the upper structure of the melting pool, the pool wall bricks and paving bricks of the working pool, and the material channel.
AZS-36 Bricks
In addition to having the same eutectic body as the AZS33 bricks, AZS36 brick is suitable for areas with high liquid glass flow rate and high temperature, such as melting pool wall bricks, paving bricks, charging port bricks, etc., because of the increase of more interlocking zirconia crystals and the decrease of glass phase content.
AZS-41 Bricks
AZS41 bricks contains more uniformly distributed zirconia crystals besides the eutectic of silicon oxide and aluminum oxide. In the zirconia corundum brick system, its corrosion resistance is the best. Therefore, the key parts of the glass furnace were selected to balance the life of these parts with that of other parts.
O AZS41 é o produto mais excelente da série AZS de fusão e fundição, com resistência extremamente elevada à corrosão do vidro líquido e temperatura de infiltração da fase vítrea extremamente elevada, e poluição extremamente baixa para o vidro líquido. É amplamente utilizado em peças-chave como a parede do tanque, canto de entrada de alimentação, orifício de fluxo, cume do forno, borbulhamento do fundo do tanque e todos os fornos de fusão eléctrica no ponto quente do forno de vidro.
AZS-36S Bricks
Os tijolos AZS de fusão e fundição com baixo teor de silício e baixo teor de sódio têm as caraterísticas de baixo teor de fase vítrea, alta temperatura de infiltração da fase vítrea, boa estabilidade a altas temperaturas e forte resistência à corrosão do vidro líquido. São refractários de fusão e fundição para a realização de isolamento térmico global, conservação de energia e longa vida útil do forno.