The rheological properties of CA50 are well adapted for all types of placing methods, particularly for casting and gunning. It is recommended for applications where rapid hardening propertes and excellent mechanical performances.
KERUI CA50 products are manufactured by sintering process in rotary kiln, represented by three product types A600. A700 and A900.
CA50-A600: A600 product has rapid hardening properities and high hydration exothermic rate, it’ s widely recommended for conventional high cement castables such as high performance alkali resistance castables, high alumina castables and slag-stopping ball, etc.
CA50-A700: In comparison with A600, A700 product has lower impurities level, stable hardening properties and rapid strength development, it is recommended mainly to be used in low cement castables.
CA50-A900: A900 product is produced with selection of high purity materials, the alumina content of A900 is higher than other grades, and impurity oxides as like SiO2, Fe203 content is lower than that of A600 and A700. So, it is widely recommended for applications where stable hardening properties, good working ability and excellent mechanical performance are required.
Notas: cimento refratário = cimento de alta alumina = cimento de aluminato de cálcio
【Physical and chemical indicators】
| Brand | A600 | A600 | A700 | A700 | A900 | A900 |
| Refractory cement Types | Gama habitual | Limite de especificação | Gama habitual | Limite de especificação | Gama habitual | Limite de especificação |
| SiO2, % | 7.8-8.3 | ≤9.0 | 7.0-7.5 | ≤8.0 | 5.0-5.5 | ≤6.0 |
| Al203, % | 50.0-51.0 | ≥50.0 | 50.5-51.5 | ≥50.0 | 53.5-54.5 | ≥53.0 |
| Fe203, % | 1.5-2.5 | ≤3.0 | 1.5-2.5 | ≤3.0 | 1.5-2.0 | ≤3.0 |
| R20, % | – | ≤0.5 | – | ≤0.5 | – | ≤0.5 |
| S-, % | – | ≤0.2 | – | ≤0.2 | – | ≤0.2 |
| CI-, % | – | ≤0.06 | – | ≤0.06 | – | ≤0.06 |
| 325M(%) | – | ≤20 | – | ≤15 | – | ≤8 |
| Superfícies específicas, ㎡/kg | – | ≥320 | – | ≥350 | – | ≥380 |
| Tempo de regulação, min | ||||||
| Tempo de regulação inicial IS | 50-120 | ≥30 | 50-120 | ≥30 | 150-210 | ≥150 |
| Tempo de regulação final FS | 90-180 | ≤360 | 120-210 | ≤360 | 210-300 | ≤360 |
| Resistência à flexão, Mpa | ||||||
| 1d | – | ≥5.5 | – | ≥6.5 | – | ≥8.5 |
| 3d | – | ≥6.5 | – | ≥7.5 | – | ≥9.5 |
| Resistência à compressão, Mpa | ||||||
| 1d | 45-55 | ≥40 | 50-60 | ≥50 | 70-75 | ≥70 |
| 3d | 50-60 | ≥50 | 60-65 | ≥60 | 80-85 | ≥80 |
【Informações adicionais】
Principal phase: CA
Secondary phase: C12A7、C2AS、CT
Pyrometric cone equivalent: 1400-1450℃
Bulk density: 900-1000kg/m3
Specific gravity: 2.9-3.1g/cm3
Shelf Life: 3 months
【Embalagem e armazenamento】
Método de embalagem: Embalagem padrão para exportação
Sacos de papel: 25/50kg
Sacos grandes: 1,0/1,5mt
Storage tips: Calcium aluminate cement CA50 must be stored in dry conditions, off the ground. In this case, it will retain its properties for at least 2 months. In many instances. experience has demonstrated that properties are retained for more than 3 months.