Introduction to fused zirconium corundum brick(AZS Bricks):
Electric fused zirconium corundum bricks, also called Fused AZS bricks, are arranged according to the three chemical components in the phase diagram of Al2O3-ZrO2-SiO2. Among them, 33, 36 and 41 are named according to the content of Al2O3. For example, AZS33 refers to the fused zirconium corundum brick with an alumina content of 33%.
Parameters of Kerui Fused AZS Bricks
| ltem | AZS-33 | AZS-33 | AZS-36 | AZS-36 | AZS-41 | AZS-41 |
| – | Y | H | Y | H | Y | H |
| Al2O3, ≥ | 50 | 50.5 | 48 | 49 | 45 | 45.5 |
| ZrO2, ≥ | 32.0 | 32.0 | 35.0 | 35.0 | 40.0 | 40.0 |
| SiO2, ≤ | 15.0 | 16.0 | 13.5 | 13.5 | 13.0 | 12.0 |
| Na2O, ≤ | 1.5 | 1.5 | 1.4 | 1.4 | 1.3 | 1.3 |
| BD, PT.QX, ≥ | 3.40 | 3.30 | 3.45 | 3.40 | 3.55 | 3.50 |
| BD, MS, ≤ | 3.50 | 3.45 | 3.60 | 3.55 | 3.70 | 3.65 |
| BD, WS, ≤ | 3.60 | 3.55 | 3.70 | 3.65 | 3.80 | 3.75 |
AZS-33 Bricks
AZS-33 bricks has good corrosion resistance to liquid glass, is not easy to produce stones or other defects, and has low possibility of producing small bubbles. Therefore, AZS-33 bricks are widely used in glass kilns, mainly applicable to the upper structure of the melting pool, the pool wall bricks and paving bricks of the working pool, and the material channel.
AZS-36 Bricks
In addition to having the same eutectic body as the AZS33 bricks, AZS36 brick is suitable for areas with high liquid glass flow rate and high temperature, such as melting pool wall bricks, paving bricks, charging port bricks, etc., because of the increase of more interlocking zirconia crystals and the decrease of glass phase content.
AZS-41 Bricks
AZS41 bricks contains more uniformly distributed zirconia crystals besides the eutectic of silicon oxide and aluminum oxide. In the zirconia corundum brick system, its corrosion resistance is the best. Therefore, the key parts of the glass furnace were selected to balance the life of these parts with that of other parts.
AZS41 - самый превосходный продукт в серии AZS для плавки и литья, обладающий чрезвычайно высокой устойчивостью к коррозии жидкого стекла и чрезвычайно высокой температурой просачивания стеклофазы, а также чрезвычайно низким уровнем загрязнения жидкого стекла. Он широко используется в ключевых частях, таких как стенка резервуара, угол загрузочного отверстия, отверстие потока, гребень печи, барботирование дна резервуара и все электрические плавильные печи в горячей точке стекловаренной печи.
AZS-36S Bricks
Плавильно-литейные кирпичи AZS с низким содержанием кремния и натрия обладают такими характеристиками, как низкое содержание стеклофазы, высокая температура просачивания стеклофазы, хорошая высокотемпературная стабильность и сильная устойчивость к коррозии жидкого стекла. Это плавильные и литейные огнеупоры для обеспечения общей теплоизоляции, энергосбережения и длительного срока службы печи.